Exhaust gas treatment system

ABSTRACT

It is intended to provide an exhaust gas treatment system, which allows for VOC removal at lower temperatures and thereby improves the durability of catalysts and suppresses carbon monoxide generation at the final outlet of the system. The present invention provides a treatment system of an exhaust gas containing a nitrogen oxide, carbon monoxide, and a volatile organic compound comprising: an exhaust gas treatment means for removing the nitrogen oxide by reduction with ammonia and partially oxidizing the VOC to CO; and a CO/VOC removal means for oxidizing the CO and partially unreacted VOC, in this order from the upstream flow of the exhaust gas.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of U.S. application Ser. No. 11/705,601, filed Feb. 13, 2007 now U.S. Pat. No. 8,124,021, based upon and claims the benefit of priority of prior Japanese Patent Application No. 2006-054811, filed Mar. 1, 2006, the entire contents of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to an exhaust gas treatment system.

2. Description of the Related Art

NOx, SOx, carbon monoxide (CO), and volatile organic compounds (VOCs) such as saturated hydrocarbons except methane and ethane and unsaturated hydrocarbons e.g. ethylene are contained in exhaust gases discharged from industrial devices of various types (e.g. automobile engines, air craft gas turbines, and gas turbines for power generation), chemical plants, factories of various types, and so on. Such components contained in exhaust gases have been treated by adopting a system using catalysts for the removal of CO, VOCs and the like in combination with a denitration catalyst.

The current system requires the catalysts for the removal of CO, VOCs and the like at an upstream stage with a higher temperature because the catalysts have to be exposed to a temperature higher than 400° C. for improving the conversion rates of CO and VOC (see e.g., Japanese Patent Provisional Publication No. 10-309462). However, the system operation under the high temperature presents problems in terms of the durability of the apparatus such as the deterioration of the catalysts for the removal of CO, VOCs and the like.

Among VOCs, particularly, saturated hydrocarbons (NMHCs) such as propane shows a low burning velocity in the presence of the catalysts for the removal of CO, VOCs and the like conventionally placed at the upstream stage. Most of the saturated hydrocarbons passed through the upstream stage remaining unreacted unless the temperature is increased to 550° C. which is the upper limit of the suitable temperature range described in Japanese Patent Provisional Publication No. 10-309462. As a result, the saturated hydrocarbons unreacted are partially oxidized with the denitration catalyst placed downstream at 400° C. or lower and become a source of carbon monoxide at the final outlet of the system.

An object of the present invention is to provide an exhaust gas treatment system, which allows for VOC removal at lower temperatures and thereby improves the durability of catalysts and suppresses carbon monoxide generation at the final outlet of the system.

SUMMARY OF THE INVENTION

The present invention has been completed for attaining the object. Specifically, an exhaust gas treatment system according to the present invention may be a treatment system of an exhaust gas containing a nitrogen oxide (NOx), carbon monoxide, and a volatile organic compound for attaining the object comprising: exhaust gas treatment means for removing the nitrogen oxide by reduction with ammonia (NH₃) and partially oxidizing the volatile organic compound (VOC) to carbon monoxide (CO); and CO/VOC removal means for oxidizing the CO and partially unreacted VOC, in this order from the upstream side of a gas flow.

It may be preferred that the exhaust gas treatment system according to the present invention further comprises secondary reductive denitration means downstream of the CO/VOC removal means.

An exhaust gas treatment system according to the present invention may be a treatment system of an exhaust gas containing carbon monoxide and a volatile organic compound comprising: exhaust gas treatment means for partially oxidizing the VOC to CO; and CO/VOC removal means for oxidizing the CO and partially unreacted VOC, in this order from an upstream flow of the exhaust gas.

For the exhaust gas treatment system according to the present invention, it is preferred that the exhaust gas treatment means comprise an exhaust gas treating catalyst comprising 60% or more by weight TiO₂, 0 to 8% by weight V₂O₅, and 3 to 20% by weight WO₃ with respect to the total weight thereof.

For the exhaust gas treatment system according to the present invention, it may be preferred that the CO/VOC removal means comprise a CO/VOC removal catalyst in which a porous inorganic compound layer comprising a noble metal and having reactivity to the CO and VOC is formed on a honeycomb substrate made of a porous inorganic compound unreactive to the nitrogen oxide, CO, and VOC.

For the exhaust gas treatment system according to the present invention, it is preferred that the CO/VOC removal means comprises a CO/VOC removal catalyst in which a porous inorganic compound layer comprising a noble metal is formed on a honeycomb substrate comprising an NMHC oxidation catalyst.

For the exhaust gas treatment system according to the present invention, it is preferred that the CO/VOC removal means comprise a CO/VOC removal catalyst in which a porous inorganic compound layer comprising a noble metal and in which an NMHC oxidation catalyst is formed on a honeycomb substrate comprising an NMHC oxidation catalyst.

For the exhaust gas treatment system according to the present invention, it is preferred that the porous inorganic compound layer have a thickness of 4 μm to 80 μm.

For the exhaust gas treatment system according to the present invention, it is preferred that the noble metal be platinum (Pt), and the Pt have an average particle size of 1 to 15 nm.

For the exhaust gas treatment system according to the present invention, it is preferred that the porous inorganic compound layer have a BET specific surface of 50 m²/g or more and hold the noble metal within 50 μm deep from the surface thereof.

For the exhaust gas treatment system according to the present invention, it is preferred that the CO/VOC removal means be operated at a temperature of 200 to 400° C.

According to the present invention, an exhaust gas treatment system with excellent durability, which is improved in the conversion rates of carbon monoxide and volatile organic compounds contained in exhaust gases under relatively low temperature conditions, can be obtained.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow diagram of Example 1.

FIG. 2 is a flow diagram of Example 2.

FIG. 3A is a flow diagram of Example 3.

FIG. 3B is a flow diagram of comparative Example 1.

FIG. 4A is a flow diagram of Examples 4 and 6 to 8.

FIG. 4B is a flow diagram of comparative Examples 2 and 3.

FIG. 5 is a flow diagram of Example 5.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Hereinafter, the present invention will be described in detail.

An exhaust gas treatment system according to the present invention may be a system for treating an exhaust gas containing NOx, CO and VOC.

The “volatile organic compound” generally refers to hydrocarbons except methane and ethane.

The exhaust gas treatment system of the present invention may be a system comprising exhaust gas treatment means on the upstream side of a gas flow.

The exhaust gas treatment means may be an element responsible for removing the nitrogen oxide by reduction with ammonia as shown in (Formula 1) and partially oxidizing the VOC to CO as shown in (Formula 2) in the exhaust gas treatment system. 4NO+4NH₃+O₂→4N₂+6H₂O  (Formula 1) CmHn+(2m+n/4)O₂ →mCO+(n/2)H₂O  (Formula 2)

The reducing agent for the nitrogen oxide is not limited to ammonia but may include compounds which generate ammonia in the gas phase or in the exhaust gas treatment means. The reducing agent to be used is besides ammonia, for example, urea water ((NH₂)₂CO), which generates ammonia through hydrolysis as shown in (Formula 3). (NH₂)₂CO+H₂O→>2NH₃+CO₂  (Formula 3)

Alternatively, the exhaust gas treatment means may be an element responsible for partially oxidizing the VOC to CO in the exhaust gas treatment system. In this case, the exhaust gas treatment means may not employ the function of removing the nitrogen oxide by reduction with ammonia.

The exhaust gas treatment means can comprise an exhaust gas treating catalyst such as a TiO₂—WO₃ compound or a TiO₂—V₂O₅—WO₃ compound. Besides, the exhaust gas treatment means that can be applied to the present invention may be a catalyst such as a TiO₂—V₂O₅-molybdenum oxide (MoO₃) compound or a TiO₂—V₂O₅ compound, which is used for removing nitrogen oxides by reduction with ammonia or urea. In the process of developing a technique for removing nitrogen oxides by reduction with ammonia in the presence of the exhaust gas treating catalyst such as a TiO₂—WO₃ compound or a TiO₂—V₂O₅—WO₃ compound, we have found that the exhaust gas treating catalyst also has a function of partially oxidizing to CO, VOCs including unsaturated hydrocarbon compounds such as C₂H₄ and C₆H₆ and saturated hydrocarbon compounds such as C₃H₈ and C₄H₁₀, as shown in, for example, (Formula 4). Depending on a VOC component, both partial oxidation and complete oxidation reactions proceed as shown in (Formula 5) and (Formula 6). C₃H₈+7/2O₂→3CO+4H₂O  (Formula 4) C₆H₆+9/2O₂→6CO+3H₂O  (Formula 5) C₆H₆+15/2O₂→6CO₂+3H₂O  (Formula 6)

Since this function of partial oxidation to CO is independent of the use of the function of removing the nitrogen oxide by reduction with ammonia, the exhaust gas treatment means has become an important element responsible for the function of partially oxidizing the VOC to CO by using the exhaust gas treating catalyst as the exhaust gas treatment means.

Exhaust gases discharged from gas turbines for power generation, chemical plants and so on inevitably contain nitrogen oxides. Under current strict emission control, an exhaust gas treating catalyst which removes nitrogen oxides by reduction with ammonia may be commonly placed in such facilities. CO can be easily oxidized with a CO/VOC removal catalyst at low temperatures. Thus, the partial oxidation to CO and subsequent removal of VOC including poorly combustible saturated hydrocarbons by using the industrially utilized catalyst for exhaust gas treatment in combination with the CO/VOC removal catalyst are exceedingly efficient in terms of cost.

When the exhaust gas treating catalyst comprises the TiO₂—V₂O₅—WO₃ compound, it may be preferred that the exhaust gas treating catalyst has 60% or more by weight TiO₂, 0 to 8% by weight V₂O₅, and 3 to 20% by weight WO₃, with respect to the total weight thereof. In this context, the exhaust gas treating catalyst may have 90% by weight TiO₂ as the upper limit.

It may be further preferred that the exhaust gas treating catalyst have a 70% or more by weight TiO₂, 3 to 8% by weight V₂O₅, and 8 to 20% by weight WO₃, with respect to the total weight thereof. The exhaust gas treating catalyst having a larger V₂O₅ content can partially oxidize VOC including poorly combustible saturated hydrocarbons to CO to a higher extent. On the other hand, it has been shown in Example 8 below that the exhaust gas treating catalyst having a WO₃ content of 20% by weight can partially oxidize the VOC to CO to a sufficient extent even if the exhaust gas treating catalyst has 0% by weight V₂O₅.

Thus, V₂O₅ can be an arbitrary component when the WO₃ content ranges from 16 to 20% by weight.

The exhaust gas treatment system of the present invention is a system comprising CO/VOC removal means downstream of the exhaust gas treatment means.

The CO/VOC removal means is an element responsible for a function of oxidizing the CO and VOC in the exhaust gas treatment system.

The CO/VOC removal means may include CO/VOC removal means in which a γ-Al₂O₃ layer comprising a noble metal is formed on a cordierite honeycomb substrate conventionally known in the art, CO/VOC removal means in which a γ-Al₂O₃ layer comprising a noble metal is formed on a solid honeycomb substrate mainly comprising TiO₂, and CO/VOC removal means in which γ-Al₂O₃ comprising a noble metal and an unburned hydrocarbon oxidation catalyst described later are layered or contained.

For the exhaust gas treatment system of the present invention, it may be preferred that the CO/VOC removal means comprises a noble metal and an unburned hydrocarbon (NMHC) oxidation catalyst.

The noble metal is not particularly limited as long as it can promote the oxidation of CO and unsaturated and saturated hydrocarbons. The noble metal may be preferably at least one member selected from the group consisting of, for example, Ir, Rh, Ru, Pt, Pd, Ag, Au, and oxides thereof, and may be more preferably Pt, Pd, or Ru, even more preferably Pt.

The noble metal may be prepared first as an aqueous solution of a noble metal salt comprising a nitrate, chloride, acetate, or complex salt dissolved therein. The noble metal salt aqueous solution may contain a pH buffer solution for stabilizing the rate of metal ion reduction during the colloid production described hereinafter.

A metal colloid solution containing the noble metal can be obtained by adding the noble metal salt aqueous solution to a mixture comprising a reducing agent (which includes: organic acids such as sodium citrate, potassium citrate, acetic acid, formic acid, and malic acid; alcohols such as methanol, ethanol, and propanol; and ethers such as diethyl ether), water, and a polymer material such as polyvinyl alcohol, polyvinylpyrrolidone, or polymethylvinyl ether and heating the resulting mixture solution to about 80 to about 95° C.

The average particle size of the Pt colloid contained in the colloid solution may be preferably 1 to 15 nm. The upper limit of the average particle size may be more preferably 3 nm. In the present specification, the average colloid particle size can be measured with a TEM photograph.

In the present specification, the NMHC oxidation catalyst is an oxidation catalyst that can oxidize unburned saturated hydrocarbons to at least carbon monoxide.

The NMHC oxidation catalyst can be made of, for example, the TiO₂—V₂O₅—WO₃ compound or TiO₂—WO₃ compound as the exhaust gas treating catalyst, which may be used in a selective catalytic reduction (SCR) method of NOx such as denitration with ammonia or urea.

The CO/VOC removal means can be obtained as a CO/VOC removal catalyst, for example, by allowing the noble metal-containing colloid solution to be carried by a porous inorganic compound, converted into slurry, and layered onto a honeycomb substrate comprising an NMHC oxidation catalyst.

The porous inorganic compound which constitutes the carrier may be preferably at least one selected from the group consisting of SiO₂, Al₂O₃, TiO₂, ZrO₂, SiO₂—Al₂O₃, TiO₂—SiO₂, TiO₂—Al₂O₃, TiO₂—ZrO₂, SO₄/ZrO₂, SO₄/TiO₂, SO₄/TiO₂—ZrO₂, metallosilicate, and zeolites such as β-zeolite.

The conversion to slurry can be performed, for example, by allowing the noble metal-containing colloid solution to be carried by the porous inorganic compound by a spray-drying method, sintered, and then pulverized with a ball mill.

The concentration of the slurry obtained by the above conversion method may be preferably 5% to 20% by weight, more preferably 10% to 15% by weight. The concentration of the slurry can be obtained by measuring the weight of the dried slurry.

The CO/VOC removal catalyst can be obtained, for example, by wash-coating the slurry onto a honeycomb substrate comprising an NMHC oxidation catalyst.

The thickness of the porous inorganic compound layer formed by wash-coating can be 4 μm to 80 μm when the slurry has the concentration described above. The thickness of the porous inorganic compound layer may have a preferred lower limit of 10 μm and a preferred upper limit of 20 μm. The thickness of the porous inorganic compound layer can be measured with an SEM photograph or EPMA analysis.

The obtained CO/VOC removal catalyst can have a Pt content of 0.39 g/L to 0.59 g/L (Pt Weight/Total Volume of Catalyst). The Pt content may be preferably not more than 0.53 g/L.

Alternatively, the CO/VOC removal means can be obtained as a CO/VOC removal catalyst comprises a honeycomb substrate and a porous inorganic compound layer thereon wherein the substrate comprises an NMHC oxidation catalyst and the layer comprises a noble metal and an NMHC oxidation catalyst.

The porous inorganic compound layer comprising a noble metal and an NMHC oxidation catalyst is generally formed by mixing a slurry containing a noble metal with a slurry containing an NMHC oxidation catalyst to form a mixture, wherein the slurry containing the noble metal is obtained by allowing a colloid solution containing a noble metal to be carried on a carrier; sintering the mixture; and pulverizing the sintered mixture with a ball mill.

The CO/VOC removal means can also be obtained as a CO/VOC removal catalyst in which a porous inorganic compound layer comprising a noble metal and having reactivity to the CO and VOC is formed on a honeycomb substrate made of a porous inorganic compound unreactive to the nitrogen oxide, CO, and VOC.

It may be preferred that the noble metal contained in the porous inorganic compound layer is Pt having an average particle size of 1 to 15 nm. The Pt may have an average particle size of 2 nm as the more preferred lower limit and 11 nm as the more preferred upper limit.

The average particle size of the Pt may be determined by calculating the distribution of Pt particles by a chemical adsorption method using CO pulses.

The porous inorganic compound layer may preferably have a BET specific surface of 50 m²/g or more. The porous inorganic compound layer may have a BET specific surface of 100 m²/g as the more preferred lower limit and 150 m²/g as even more preferred lower limit. The porous inorganic compound layer can have a BET specific surface of, for example, 300 m²/g as the preferred upper limit as long as the BET specific surface falls within the range described above. The porous inorganic compound having the reactivity can be a porous inorganic compound that has a specific surface of 50 m²/g or more and can bring out the reactivity of a noble metal by allowing the noble metal to be carried in a highly dispersed manner on the porous inorganic compound.

In the present specification, the BET specific surface can be measured by using a nitrogen adsorption method.

The porous inorganic compound layer may preferably have a BET specific surface of 50 m²/g or more as described above and preferably hold the noble metal within 50 μm deep from the surface thereof.

It may be preferred that 50% or more by weight of the amount of the noble metal carried on the porous inorganic compound layer is contained within 30 μm deep, more preferably 10 μm deep from the surface of the porous inorganic compound layer.

Among VOCs, particularly, saturated hydrocarbons such as propane showed a low burning velocity on the conventional catalysts for the removal of CO, VOC and the like so that the saturated hydrocarbons mostly passed therethrough in unreacted forms. As a result, the saturated hydrocarbons can be partially oxidized with a denitration catalyst placed downstream and can become a source of carbon monoxide.

When the exhaust gas treatment system of the present invention comprises the CO/VOC removal catalyst having the structure as described above, the exhaust gas treatment system can perform both the conversion of saturated hydrocarbons typified by propane to CO by combustion and the oxidation of the CO. As a result, the exhaust gas treatment system can promote the complete combustion of the saturated hydrocarbons to CO₂ on the whole and drastically reduce not only the amount of CO discharged at the downstream outlet but also the amount of VOC discharged.

Saturated hydrocarbons are not completely incombustible in the conventional catalysts for the removal of CO, VOC and the like. Therefore, it is not impossible to burn the saturated hydrocarbons such as propane if the amount of the catalysts is increased. However, it is obvious that such a case is not realistic because of huge cost of the catalysts attributed to the use of expensive Pt. On the other hand, the exhaust gas treating catalyst comprising the TiO₂—V₂O₅—WO₃ compound is composed of only base metals and is therefore quite inexpensive. Furthermore, exhaust gases discharged from automobile engines, gas turbines for power generation, chemical plants, and so on inevitably contain nitrogen oxides. Under current strict emission control, an exhaust gas treating catalyst which removes nitrogen oxides by reduction with ammonia is commonly placed in such facilities. Thus, the removal of VOC including poorly combustible saturated hydrocarbons by using the exhaust gas treating catalyst is exceedingly efficient.

Preferably, the CO/VOC removal means of the exhaust gas treatment system of the present invention may be usually operated at a temperature of 200° C. to 400° C. from the viewpoint of a balance between catalyst activity and the maintenance of the durability of the apparatus. The CO/VOC removal means may be operated at a temperature of 300° C. as the more preferred lower limit.

The exhaust gas treatment system of the present invention can remove, for example, 65% or more, 70% or more, or 73% or more of propane simultaneously with 70% or more, 98% or more, or 99% or more of CO, at 400° C.

The exhaust gas treatment system of the present invention has a sufficiently high conversion rate even under relatively low temperature conditions, as described above, and can further improve the conversion rate at higher temperatures.

The exhaust gas treatment system of the present invention can be operated under relatively low temperature conditions by placing the CO/VOC removal means downstream of the exhaust gas treatment means, as described above. As a result, the exhaust gas treatment system can improve the durability of the apparatus and so on more than before and can exceedingly reduce CO generation at the final outlet of the system.

It may be preferred that the exhaust gas treatment system of the present invention further comprises secondary reductive denitration means downstream of the CO/VOC removal means.

The secondary reductive denitration means may be placed to remove NOx generated from unreacted ammonia for nitrogen oxide reduction, which has been discharged from the exhaust gas treatment means and oxidized in the CO/VOC removal means placed downstream.

The secondary reductive denitration means is distinguished from the exhaust gas treatment means of the exhaust gas treatment system of the present invention because the secondary reductive denitration means does not require a function of removing CO. However, the secondary reductive denitration means can use the same catalyst as the exhaust gas treating catalyst described above.

EXAMPLES

Hereinafter, the present invention will be described with reference to Examples. However, the present invention is not intended to be limited to them.

Preparation Example 1

A TiO₂—V₂O₅—WO₃ catalyst (TiO₂:V₂O₅:WO₃=80:3:8 by weight) used as an exhaust gas treating catalyst was prepared as follows: ammonia water having an NH₃ content of 25% was added to 3600 g of metatitanic acid slurry (TiO₂ content of 30% by weight) to adjust pH to 6.5. A powder of ammonium paratungstate was added thereto at 8% by weight in terms of WO₃ and kneaded in a wet process for 2 hours. The mixture was then dried and further sintered at 550° C. for 5 hours to obtain a powder of titanium oxide and tungsten oxide. An aqueous solution of ammonium metavanadate was added at 3% by weight in terms of V₂O₅ to this powder and sufficiently mixed. The mixture was then dried and sintered at 450° C. for 4 hours to obtain a TiO₂—V₂O₅—WO₃ powder (A). In a kneader, 1000 g of the powder (A), 25 g of carboxymethylcellulose, and 12.5 g of polyethylene oxide were placed and kneaded for 30 minutes after the addition of an appropriate amount of water. The kneaded mixture was then extrusion-molded so that the molded form has a cross-section size of 50 mm×50 mm perpendicular to a gas flow, then dried, and sintered at 500° C. for 5 hours.

Preparation Example 2

A TiO₂—WO₃ catalyst (TiO₂:WO₃=75:20 by weight) used as an exhaust gas treating catalyst was prepared as follows: ammonia water having an NH₃ content of 25% was added to 3600 g of metatitanic acid slurry (TiO₂ content of 30% by weight) to adjust pH to 6.5. A powder of ammonium paratungstate was added thereto at 20% by weight in terms of WO₃ and kneaded in a wet process for 2 hours. The mixture was then dried and further sintered at 550° C. for 5 hours to obtain a TiO₂—WO₃ powder (B). In a kneader, 1000 g of the powder (B), 25 g of carboxymethylcellulose, and 12.5 g of polyethylene oxide were placed and kneaded for 30 minutes after the addition of an appropriate amount of water. The kneaded mixture was extrusion-molded so that the molded form has a cross-section size of 50 mm×50 mm perpendicular to a gas flow, then dried, and sintered at 500° C. for 5 hours.

Preparation Example 3

(I) Preparation of Pt Colloid Solution

A metal colloid solution containing a single noble metal Pt was prepared to perform Examples 4 to 8 and Comparative Example 2. The metal colloid solution was prepared according to the following procedures:

(1) Ion-exchange water and ethanol as a reducing agent were prepared. The ratio of ion-exchange water/reducing agent by volume was 1/1;

(2) 1.5 Liter of the reducing agent (reducing agent solution) was mixed with 1.5 Liter of the ion-exchange water to make 1 Liter of a mixture solution. Moreover, 32 g of polyvinyl alcohol as a polymer material was added thereto. The aqueous solution was kept at 80° C. and boiled for 1 hour to thereby remove dissolved oxygen; (3) 0.1 Liter of a metal salt corresponding to each active metal was added to the mixture solution to prepare a Pt-containing aqueous solution in which 75 mmol active metal was contained; and (4) The Pt-containing aqueous solution was kept at 80° C. and reduced for 5 hours to thereby obtain 0.5% by weight of a Pt colloid solution (average colloid particle size of 2 to 3 nm). (II) Production of Catalyst for CO/VOC Removal Using Pt Colloid Solution

A γ-Al₂O₃ carrier having a BET specific surface of 113 m²/g was pulverized with a ball mill. The obtained slurry (concentration of 10% by weight) was then layered on a cordierite honeycomb substrate so that the amount of the slurry coated was 42.5 to 57.5 g/m² with respect to the surface area of the honeycomb substrate. Then, 4000 cc of an aqueous solution containing 0.07% by weight of the Pt colloid with respect to the whole weight of the aqueous solution was prepared. A predetermined amount of Pt was carried on the honeycomb substrate (50 mm long×50 mm wide×50 mm high) by dipping the honeycomb substrate in the aqueous solution for 30 minutes. The catalyst after coating was dried at 110° C. and then sintered at 500° C. for 5 hours to obtain a CO/VOC removal catalyst (1). The coating layer thickness of the obtained catalyst for CO/VOC removal fell in the range of 30 to 80 μm due to the uneven layering of the slurry. When the Pt colloid is carried on the γ-Al₂O₃, the holding conditions depend on the concentration of the polymer material. Since the uneven distribution of the Pt colloid due to the concentration of the polymer material was apparently observed, the evenly colored catalyst was subjected to a reaction rate evaluation test described later.

The Pt particle size after sintering was determined by calculating the degree of Pt dispersion by a chemical adsorption method using CO pulses.

Preparation Example 4

A spray-drying method was used to allow 8800 g of the noble metal-containing colloid solution to be carried on 1500 g of a γ-Al₂O₃ carrier having a BET specific surface of 113 m²/g. The carrier was sintered at 500° C. for 5 hours and further pulverized with a ball mill at 100 rpm for 8 hours to obtain slurry (concentration of 10% by weight). The obtained slurry was layered on a honeycomb substrate comprising an NMHC oxidation catalyst so that the amount of the slurry coated was 8.5 to 11.5 g/m² with respect to the surface area of the honeycomb substrate. The catalyst after coating was dried at 110° C. and then sintered at 500° C. for 5 hours to obtain a CO/VOC removal catalyst (2). The coating layer thickness of the obtained catalyst for CO/VOC removal fell in the range of 4 to 20 μm due to the uneven layering of the slurry.

Preparation Example 5

A spray-drying method was used to allow 8800 g of the noble metal-containing colloid solution to be carried on 1500 g of a γ-Al₂O₃ carrier having a BET specific surface of 113 m²/g. The carrier was sintered at 500° C. for 5 hours and further pulverized with a ball mill at 100 rpm for 8 hours. The obtained slurry was mixed at a 7:3 ratio by weight with slurry obtained by pulverizing an NMHC oxidation catalyst with a ball mill at 100 rpm for 8 hours, to obtain mixture slurry (concentration of 10% by weight). The obtained mixture slurry was layered on a honeycomb substrate comprising an NMHC oxidation catalyst so that the amount of the slurry coated was 11.9 to 16.1 g/m² with respect to the surface area of the honeycomb substrate. The catalyst after coating was dried at 110° C. and then sintered at 500° C. for 5 hours to obtain a CO/VOC removal catalyst (3). The coating layer thickness of the obtained catalyst for CO/VOC removal fell in the range of 6 to 30 μm due to the uneven layering of the slurry.

EXAMPLE 1

The exhaust gas treating catalyst obtained in Preparation Example 1 was subjected to an oxidation reaction test of VOC (CH₄, C₂H₆, C₃H₈, and C₄H₁₀). In the oxidation reaction test, the hydrocarbon concentrations (shown below) on the upstream side of an exhaust gas flow from kerosene combustion and close behind the exhaust gas treating catalyst were analyzed with an FID gas chromatograph manufactured by Shimadzu Corp. The results are shown in Table 1.

Linear flow rate: 2.0 Nm/s, CO: 9400 ppm, CH₄: 8450 ppm, C₂H₆: 650 ppm, C₃H₈: 260 ppm, C₄H₁₀: 190 ppm, O₂: 10%, NOx, CO₂, H₂O, and N₂: uncontrolled, space velocity (GHSV) of catalyst for exhaust gas treatment: 7,500 h⁻¹, operation temperature: 200° C., 250° C., 300° C., 350° C., and 400° C.

EXAMPLE 2

The exhaust gas treating catalyst obtained in Preparation Example 1 was subjected to an oxidation reaction test of VOC (C₆H₆ and C₆H₁₂). In the oxidation reaction test, the C₆H₆ and C₆H₁₂ concentrations on the upstream side of an exhaust gas flow from kerosene combustion and the C₆H₆ and C₆H₁₂ concentrations close behind the exhaust gas treating catalyst were analyzed with an FID gas chromatograph manufactured by Shimadzu Corp. The results are shown in Table 2.

Linear flow rate: 2.0 Nm/s, C₆H₆: 300 ppm, C₆H₁₂ (cyclohexane): 700 ppm, O₂: 5%, NOx: 1500 ppm, NH₃: 1380 ppm, CO₂, H₂O, and N₂: uncontrolled, GHSV of catalyst for exhaust gas treatment: 2,800 h⁻¹, operation temperature: 300° C.

TABLE 1 Catalyst for exhaust gas Concentration at inlet of catalyst Concentration at outlet of catalyst treatment Tempera- for exhaust gas treatment (ppm) for exhaust gas treatment (ppm) Reaction rate (%) (% by weight) ture (° C.) CO CH₄ C₂H₆ C₃H₈ C₄H₁₀ CO CH₄ C₂H₆ C₃H₈ C₄H₁₀ CO CH₄ C₂H₆ C₃H₈ C₄H₁₀ Ex. 1 TiO2(80) 400 9400 8450 650 260 190 10860 8380 530 90 30 — 0.8 18.5 65.4 84.2 V2O5(3) 350 9400 8450 650 260 190 10490 8450 570 150 40 — 0.0 12.3 42.3 78.9 WO3(8) 300 9400 8450 650 260 190 10160 8450 600 200 70 — 0.0 7.7 23.1 63.2 250 9400 8450 650 260 190 9830 8450 620 230 120 — 0.0 4.6 11.5 36.8 200 9400 8450 650 260 190 9560 8450 640 240 170 — 0.0 1.5 7.7 10.5

TABLE 2 Catalyst for exhaust gas Concentration at inlet of catalyst Concentration at outlet of catalyst treatment Tempera- for exhaust gas treatment (ppm) for exhaust gas treatment (ppm) Reaction rate (%) (% by weight) ture (° C.) C₆H₅ C₆H₁₂ CO C₆H₆ C₆H₁₂ CO C₆H₆ C₆H₁₂ CO Ex. 2 TiO2(80) 300 300 700 0 2.6 2.6 3080 99.1 99.6 — V2O5(3) WO3(8)

Tables 1 and 2 demonstrated that the VOCs of various kinds are partially oxidized to CO in the zone of the exhaust gas treating catalyst in Examples 1 to 2.

EXAMPLE 3

A two-stage exhaust gas treatment system of the present invention was obtained by allowing the exhaust gas treating catalyst obtained in Preparation Example 1 to be placed upstream and allowing a waveform metal honeycomb catalyst commercially available from Engelhard Corp. as a CO/VOC removal catalyst to be placed downstream.

The system of Example 3 thus prepared was subjected to a reaction rate evaluation test under initial conditions described below, wherein each gas concentration on the upstream side of an exhaust gas flow from kerosene combustion, close behind the exhaust gas treating catalyst, and at the final outlet of the system was measured with an FID gas chromatograph manufactured by Shimadzu Corp. The results are shown in Table 3.

Linear flow rate: 2.5 Nm/s, CO: 63 ppm, C₃H₈: 13 ppm, C₂H₄: 13 ppm, O₂: 15%, CO₂, H₂O, and N₂: uncontrolled, GHSV of catalyst for exhaust gas treatment: 7,500 h⁻¹, GHSV of catalyst for CO/VOC removal: 59,000 h⁻¹, operation temperature: 200° C., 250° C., 300° C., 350° C., and 400° C.

Comparative Example 1

A waveform metal honeycomb catalyst commercially available from Engelhard Corp. was used alone as a CO/VOC removal catalyst without the use of the exhaust gas treating catalyst and subjected to a reaction rate evaluation test under initial conditions described below, wherein each gas concentration on the upstream side of an exhaust gas flow from kerosene combustion and close behind the CO/VOC removal catalyst was measured with an analyzer (FID gas chromatograph manufactured by Shimadzu Corp).

Linear flow rate: 2.5 Nm/s, CO: 63 ppm, C₃H₈: 13 ppm, C₂H₄: 13 ppm, O₂: 15%, CO₂, H₂O, and N₂: uncontrolled, GHSV of catalyst for CO/VOC removal: 59,000 h⁻¹, operation temperature: 400° C. and 500° C. The results are shown in Table 3.

TABLE 3 Catalyst for exhaust gas Catalyst for Reaction rate in zone of catalyst treatment CO/VOC Tempera- for exhaust gas treatment (%) Total reaction rate (%) (% by weight) removal ture (° C.) CO CH₄ C₂H₆ C₃H₈ C₄H₁₀ CO CH₄ C₂H₆ C₃H₈ C₄H₁₀ Ex. 3 TiO2(80) Commercially 400 — 0.8 18.5 65.4 84.2 99.9 — — 67.8 — V2O5(3) available 350 — 0.0 12.3 42.3 78.9 99.8 — — 44 — WO3(8) catalyst 300 — 0.0 7.7 23.1 63.2 99.3 — — 23.1 — 250 — 0.0 4.6 11.5 36.8 97.6 — — 11.5 — 200 — 0.0 1.5 7.7 10.5 93.5 — — 7.7 — Com. None Commercially 500 — — — — — 100 — — 57 — Ex. 1 available 400 — — — — — 99.9 — — 10 — catalyst

Table 3 demonstrated that the use of only the zone of the catalyst for CO/VOC removal in Comparative Example 1, which without lacks the use of the exhaust gas treating catalyst, requires increasing the temperature of the zone of the CO/VOC removal catalyst to higher than 500° C. or higher for obtaining attaining the same reaction rate of VOC as that at 400° C. in Example 3.

EXAMPLE 4

A two-stage-structuretwo-stage exhaust gas treatment system of the present invention was obtained by allowing the TiO₂—V₂O₅—WO₃ catalyst (TiO₂:V₂O₅:WO₃=80:3:8 by weight) obtained in Preparation Example 1 as an exhaust gas treating catalyst to be placed upstream and allowing the CO/VOC removal catalyst obtained in Preparation Example 3 to be placed downstream of the exhaust gas treating catalyst.

Comparative Example 2

A two-stage-structuretwo-stage exhaust gas treatment system for comparison was obtained by allowing the CO/VOC removal catalyst obtained in Preparation Example 3 to be placed on the upstream side of an exhaust gas flow and allowing the exhaust gas treating catalyst obtained in Preparation Example 1 to be placed downstream.

The systems of Example 4 and Comparative Example 2 thus prepared were subjected to a reaction rate evaluation test under initial conditions described below, wherein each gas concentration on the upstream side of an exhaust gas flow from kerosene combustion, immediately afterclose behind the exhaust gas treating catalyst, and at the final outlet of the system was measured with each analyzer. The results are shown in Table 5.

CO, C₃H₈, and C₂H₄ concentrations: FID gas chromatograph manufactured by Shimadzu Corp.

NOx concentration: NOx analyzer ECL-77A manufactured by Yanaco

NH₃ concentration: absorption method using dilute sulfuric acid and ion chromatograph

Linear flow rate: 2.5 Nm/s, CO: 63 ppm, C₂H₄: 13 ppm, C₃H₈: 13 ppm, NOx: 63 ppm, NH₃: 56.7 ppm, O₂: 15%, CO₂, H₂O, and N₂: uncontrolled, GHSV of catalyst for exhaust gas treatment: 7,500 h⁻¹, GHSV of catalyst for CO/VOC removal: 59,000 h⁻¹, operation temperature: 200° C., 250° C., 300° C., 350° C., and 400° C.

EXAMPLE 5

A three-stage-structurethree-stage exhaust gas treatment system of the present invention was obtained by allowing the exhaust gas treating catalyst obtained in Preparation Example 1, the CO/VOC removal catalyst obtained in Preparation Example 3, and the exhaust gas treating catalyst obtained in Preparation Example 1 as secondary reductive denitrificationnitrationmeans to be placed in this order from the upstream side of a gas flow.

The system of Example 5 thus prepared was subjected to a reaction rate evaluation test under initial conditions described below, wherein each gas concentration on the upstream side of an exhaust gas flow from kerosene combustion, immediately afterclose behind the exhaust gas treating catalyst, and at the final outlet of the system was were measured with each analyzer. The results are shown in Table 6.

CO, C₃H₈, and C₂H₄ concentrations: FID gas chromatograph manufactured by Shimadzu Corp.

NOx concentration: NOx analyzer ECL-77A manufactured by Yanaco

NH₃ concentration: absorption method using dilute sulfuric acid and ion chromatograph

Linear flow rate: 2.5 Nm/s, CO: 63 ppm, C₂H₄: 13 ppm, C₃H₈: 13 ppm, NOx: 63 ppm, NH₃: 66.2 ppm, O₂: 15%, CO₂, H₂O, and N₂: uncontrolled, GHSV of catalyst for exhaust gas treatment: 7,500 h⁻¹, GHSV of catalyst for CO/VOC removal: 59,000 h⁻¹, GHSV of the secondary reductive denitration means: 59,000 h⁻¹, operation temperature: 200° C., 250° C., 300° C., 350° C., and 400° C.

EXAMPLE 6

A two-stage-structuretwo-stage exhaust gas treatment system of the present invention was obtained by allowing the TiO₂—V₂O₅—WO₃ catalyst (TiO₂:V₂O₅:WO₃=80:3:8 by weight) prepared in Preparation Example 1 as an exhaust gas treating catalyst to be placed upstream and the CO/VOC removal catalyst obtained in Preparation Example 4 to be placed downstream of the exhaust gas treating catalyst.

EXAMPLE 7

A two-stage-structuretwo-stage exhaust gas treatment system of the present invention was obtained by allowing the TiO₂—V₂O₅—WO₃ catalyst (TiO₂:V₂O₅:WO₃=80:3:8 by weight) prepared in Preparation Example 1 as an exhaust gas treating catalyst to be placed upstream and the catalyst obtained in Preparation Example 5 to be placed downstream of the exhaust gas treating catalyst.

EXAMPLE 8

A two-stage-structuretwo-stage exhaust gas treatment system of the present invention was obtained by allowing the TiO₂—WO₃ catalyst (TiO₂:WO₃=75:20 by weight) obtained in Preparation Example 2 as an exhaust gas treating catalyst to be placed upstream and the CO/VOC removal catalyst obtained in Preparation Example 5 to be placed downstream of the exhaust gas treating catalyst.

Comparative Example 3

A two-stage-structuretwo-stage exhaust gas treatment system for comparison was obtained by allowing a CO/VOC removal catalyst obtained in the same way as in Example 6 to be placed on the upstream side of an exhaust gas flow and the same catalyst for exhaust gas treatment as in Example 1 to be placed downstream.

Each catalyst specification of the systems of Examples 4 to 8 and Comparative Examples 2 to 3 thus prepared is shown in Table 4. Moreover, the systems were subjected to a reaction rate evaluation test under initial conditions described below, wherein each gas concentration on the upstream side of an exhaust gas flow from kerosene combustion, immediately afterclose behind the exhaust gas treating catalyst, and at the final outlet of the system was measured with each analyzer. The results are shown in Tables 5 to 9.

CO, C₃H₈, and C₂H₄ concentrations: FID gas chromatograph manufactured by Shimadzu Corp.

NOx concentration: NOx analyzer ECL-77A manufactured by Yanaco

NH₃ concentration: absorption method using dilute sulfuric acid and ion chromatograph

Linear flow rate: 2.5 Nm/s, CO: 63 ppm, C₂H₄: 13 ppm, C₃H₈: 13 ppm, NOx: 63 ppm, NH₃: 56.7 ppm, O₂: 15%, CO₂, H₂O, and N₂: uncontrolled, GHSV of catalyst for exhaust gas treatment: 7,500 h⁻¹, GHSV of catalyst for CO/VOC removal: 59,000 h⁻¹, operation temperature: 200° C., 250° C., 300° C., 350° C., and 400° C.

TABLE 4 Catalyst for CO/VOC removal Coating Amount of Size of NMHC oxidation Secondary Catalyst for Carrier BET Amount of layer active active catalyst com- reductive exhaust gas (porous specific coating on thick- Active com- com- ponent in coat- denitrifica- treatment inorganic surface substrate ness com- ponent ponent ing material tion means (% by weight) Substrate oxide) (m²/g) (g/m²) (μm) ponent (g/L) (nm) (% by weight) (% by weight) Ex. 4 TiO2(80) Cordierite γ-Al₂O₃ 113 42.5~57.5 30~80  Pt 0.43~0.58 11 — — V2O5(3) honeycomb WO3(8) Ex. 5 TiO2(80) Cordierite γ-Al₂O₃ 113 42.5~57.5 30~80  Pt 0.43~0.59 11 — TiO2(80) V2O5(3) honeycomb V2O5(3) WO3(8) W03(8) Ex. 6 TiO2(80) TiO₂ solid γ-Al₂O₃ 113  8.5~11.5 4~20 Pt 0.39~0.53 11 — — V2O5(3) honeycomb WO3(8) Ex. 7 TiO2(80) TiO₂ solid γ-Al₂O₃ 113 11.9~16.1 6~30 Pt 0.39~0.53 11 TiO2(24) — V2O5(3) honeycomb V2O5(0.9) WO3(8) WO3(2.4) Ex. 8 TiO2(75) TiO₂ solid γ-Al₂O₃ 113 11.9~16.1 6~30 Pt 0.39~0.53 11 TiO2(22) — WO3(20) honeycomb WO3(6) Com. TiO2(80) Cordierite γ-Al₂O₃ 113 42.5~57.5 30~80  Pt 0.43~0.59 11 — Ex. 2 V2O5(3) honeycomb WO3(8) Com. TiO2(80) TiO₂ solid γ-Al₂O₃ 113  8.5~11.5 4~20 Pt 0.39~0.53 11 — — Ex. 3 V2O5(3) honeycomb WO3(8)

TABLE 5 Catalyst for Catalyst for Reaction rate in zone of catalyst for exhaust exhaust gas CO/VOC removal gas treatment (for Comparative Example, zone treatment Carrier (porous Tempera- of catalyst for CO/VOC removal) (%) Total reaction rate (%) (% by weight) Substrate inorganic oxide) ture (° C.) CO C₂H₄ C₃H₈ NO_(x) CO C₂H₄ C₃H₈ NO_(x) Ex. 4 TiO2(80) Cordierite γ-Al₂O₃ 400 0 — 65.4 90 100 100 71.0 90 V2O5(3) honeycomb 350 0 — 42.3 90 100 100 47.7 90 WO3(8) 300 0 — 23.1 90 100 100 26.9 90 250 0 — 11.5 89.9 99.9 99.5 13.4 89.9 200 0 — 7.7 89 99.9 99 8.4 89 Com. TiO2(80) Cordierite γ-Al₂O₃ 400 100 99.0 16.1 — 66.0 100 71.0 90 Ex. 2 V2O5(3) honeycomb 350 100 98.8 9.4 — 76.2 100 47.7 90 WO3(8) 300 100 98.5 4.9 — 86.4 100 26.9 90 250 99.9 98.1 2.1 — 92.9 99.5 13.4 89.9 200 99.9 97.6 0.7 — 95.1 99.0 8.4 89

TABLE 6 Total reaction rate (for Catalyst for Catalyst for Reaction rate in zone of catalyst for exhaust Example 5, reaction rate exhaust gas CO/VOC removal gas treatment (for Comparative Example, zone to secondary reductive treatment Carrier (porous Tempera- of catalyst for CO/VOC removal) (%) denitrification means) (%) (% by weight) Substrate inorganic oxide) ture (° C.) CO C₂H₄ C₃H₈ NO_(x) CO C₂H₄ C₃H₈ NO_(x) Ex. 5 TiO2(80) Cordierite γ-Al₂O₃ 400 0 — 65.4 100 98.4 100 73.5 99.5 V2O5(3) honeycomb 350 0 — 42.3 100 98.5 100 50.1 99.9 WO3(8) 300 0 — 23.1 99.9 99.0 100 28.5 99.9 250 0 — 11.5 99.2 99.5 99.9 14.2 99.2 200 0 — 7.7 94.7 99.6 99.9 9.0 94.7 Com. TiO2(80) Cordierite γ-Al₂O₃ 400 100 99.0 16.1 — 66.0 100 71.0 100 Ex. 2 V2O5(3) honeycomb 350 100 98.8 9.4 — 76.2 100 47.7 100 WO3(8) 300 100 98.5 4.9 — 88.4 100 26.9 99.9 250 99.9 98.1 2.1 — 92.9 99.9 13.4 99.2 200 99.9 97.6 0.7 — 95.1 99.9 8.4 94.7

TABLE 7 Catalyst for Catalyst for Reaction rate in zone of catalyst for exhaust exhaust gas CO/VOC removal gas treatment (for Comparative Example, zone treatment Carrier (porous Tempera- of catalyst for CO/VOC removal) (%) Total reaction rate (%) (% by weight) Substrate inorganic oxide) ture (° C.) CO C₂H₄ C₃H₈ NO_(x) CO C₂H₄ C₃H₈ NO_(x) Ex. 6 TiO2(80) TiO₂ solid γ-Al₂O₃ 400 0 — 65.4 90 100 100 75.2 90 V2O5(3) honeycomb 350 0 — 42.3 90 100 100 46.6 90 WO3(8) 300 0 — 23.1 90 100 99.1 24.1 90 250 0 — 11.5 89.9 99.5 90.1 11.7 89.9 200 0 — 7.7 89 99.2 72.3 7.7 89 Com. TiO2(80) TiO₂ solid γ-Al₂O₃ 400 100 98.9 28.4 — 70.9 100 75.2 90 Ex. 3 V2O5(3) honeycomb 350 100 98.2 7.4 — 75.6 100 46.6 90 WO3(8) 300 100 96.8 1.3 — 85.6 99 24.1 90 250 99.5 85.3 0.2 — 92.4 90.1 11.7 89.9 200 99.2 61.1 0.0 — 94.4 72.3 7.7 89

TABLE 8 Catalyst for Catalyst for Reaction rate in zone of catalyst for exhaust exhaust gas CO/VOC removal gas treatment (for Comparative Example, zone treatment Carrier (porous Tempera- of catalyst for CO/VOC removal) (%) Total reaction rate (%) (% by weight) Substrate inorganic oxide) ture (° C.) CO C₂H₄ C₃H₈ NO_(x) CO C₂H₄ C₃H₈ NO_(x) Ex. 7 TiO2(80) TiO₂ solid γ-Al₂O₃ 400 0 — 65.4 90 100 100 75.2 90 V2O5(3) honeycomb 350 0 — 42.3 90 100 100 46.6 90 WO3(8) 300 0 — 23.1 90 100 99.3 24.1 90 250 0 — 11.5 89.9 99.5 92.1 11.7 89.9 200 0 — 7.7 89 99.2 74.5 7.7 89 Com. TiO2(80) TiO₂ solid γ-Al₂O₃ 400 100 99.2 28.4 — 70.9 100 75.2 90 Ex. 3 V2O5(3) honeycomb 350 100 98.4 7.4 — 75.6 100 46.6 90 WO3(8) 300 100 96.6 1.3 — 85.6 99 24.1 90 250 99.5 86.8 0.2 — 92.3 92.1 11.7 89.9 200 98.9 66.3 0.0 — 94.2 74.5 7.7 89

TABLE 9 Catalyst for Catalyst for Reaction rate in zone of catalyst for exhaust exhaust gas CO/VOC removal gas treatment (for Comparative Example, zone treatment Carrier (porous Tempera- of catalyst for CO/VOC removal) (%) Total reaction rate (%) (% by weight) Substrate inorganic oxide) ture (° C.) CO C₂H₄ C₃H₈ NO_(x) CO C₂H₄ C₃H₈ NO_(x) Ex. 8 TiO2(75) TiO₂ solid γ-Al₂O₃ 400 0 — 65.4 90 100 100 75.1 90 WO3(20) honeycomb 350 0 — 42.3 90 100 100 46.5 90 300 0 — 23.1 90 100 99.3 24.1 90 250 0 — 11.5 89.9 99.5 90.6 11.7 89.9 200 0 — 7.7 89 99.2 73.3 7.7 89 Com. TiO2(80) TiO₂ solid γ-Al₂O₃ 400 100 99.1 28.2 — 70.8 100 75.1 90 Ex. 3 V2O5(3) honeycomb 350 100 98.3 7.3 — 75.6 100 46.5 90 WO3(8) 300 100 96.4 1.3 — 85.6 99 24.1 90 250 99.5 85.8 0.2 — 92.3 90.6 11.7 89.9 200 98.9 62.2 0.0 — 94.2 73.3 7.7 89

Tables 3 and 5 to 9 demonstrated that Examples 3 to 8 wherein the zone of the exhaust gas treating catalyst was placed upstream the zone of the CO/VOC removal catalyst improved the total reaction rate of CO at all the temperatures from 200 to 400° C., as compared with Comparative Examples 2 and 3 wherein the zone of the exhaust gas treating catalyst was placed downstream the zone of the CO/VOC removal catalyst. 

What is claimed is:
 1. A treatment system of an exhaust gas containing a nitrogen oxide, CO and VOC, comprising: an exhaust gas treatment means for removing the nitrogen oxide by reduction thereof with ammonia and partially oxidizing the VOC to CO, and a CO/VOC removing means for oxidizing the CO and partially unreacted VOC, in this order from an upstream flow of the exhaust gas; wherein the exhaust gas treatment means comprises an exhaust gas treating catalyst comprising 60% by weight or more TiO₂, 3 to 8% by weight V₂O₅, and 3 to 20% by weight WO₃ with respect to the total weight of the catalyst; and wherein the CO/VOC removing means comprises a CO/VOC removing catalyst comprising a honeycomb substrate and a porous inorganic compound layer thereon comprising a noble metal and an NMHC oxidation catalyst that is a TiO₂—WO₃ compound or a TiO₂—V₂O₅—WO₃ compound; and wherein the substrate comprises a porous inorganic compound unreactive to the nitrogen oxide, CO, and VOC, while the layer has reactivity to the CO and VOC.
 2. The exhaust gas treatment system of claim 1, wherein the porous inorganic compound layer has a thickness of 4 μm to 80 μm.
 3. The exhaust gas treatment system of claim 1, wherein the noble metal comprises Pt having an average particle size of 1 to 15 nm.
 4. The exhaust gas treatment system of claim 1, wherein the porous inorganic compound layer has a BET specific surface of 50 m²/g or more and holds the noble metal within 50 μm deep from a top surface thereof.
 5. A treatment system of an exhaust gas containing a nitrogen oxide, CO and VOC, comprising: an exhaust gas treatment means for removing the nitrogen oxide by reduction thereof with ammonia and partially oxidizing the VOC to CO, and a CO/VOC removing means for oxidizing the CO and partially unreacted VOC, in this order from an upstream flow of the exhaust gas; wherein the exhaust gas treatment means comprises an exhaust gas treating catalyst comprising 60% by weight or more TiO₂, 3 to 8% by weight V₂O₅, and 3 to 20% by weight WO₃ with respect to the total weight of the catalyst; and wherein the CO/VOC removing means comprises a CO/VOC removing catalyst comprising a honeycomb substrate and a porous inorganic compound layer thereon, wherein the substrate comprises an NMHC oxidation catalyst that is a TiO₇—WO₃ compound or a TiO₂—V₂O₅—WO₃ compound and the layer comprises a noble metal.
 6. The exhaust gas treatment system of claim 5, wherein the porous inorganic compound layer has a thickness of 4 μm to 80 μm.
 7. The exhaust gas treatment system of claim 5, wherein the noble metal comprises Pt having an average particle size of 1 to 15 nm.
 8. The exhaust gas treatment system of claim 5, wherein the porous inorganic compound layer has a BET specific surface of 50 m²/g or more and holds the noble metal within 50 μm deep from a top surface thereof.
 9. A treatment system of an exhaust gas containing a nitrogen oxide, CO and VOC, comprising: an exhaust gas treatment means for removing the nitrogen oxide by reduction thereof with ammonia and partially oxidizing the VOC to CO, and a CO/VOC removing means for oxidizing the CO and partially unreacted VOC, in this order from an upstream flow of the exhaust gas; wherein the exhaust gas treatment means comprises an exhaust gas treating catalyst comprising 60% by weight or more TiO₂, 3 to 8% by weight V₂O₅, and 3 to 20% by weight WO₃ with respect to the total weight of the catalyst; and wherein the CO/VOC removing means comprises a CO/VOC removing catalyst comprising a honeycomb substrate and a porous inorganic compound layer thereon, wherein the substrate comprises an NMHC oxidation catalyst that is a TiO₇—WO₃ compound or a TiO₂—V₂O₅—WO₃ compound and the layer comprises a noble metal and an NMHC oxidation catalyst.
 10. The exhaust gas treatment system of claim 9, wherein the porous inorganic compound layer has a thickness of 4 μm to 80 μm.
 11. The exhaust gas treatment system of claim 9, wherein the noble metal comprises Pt having an average particle size of 1 to 15 nm.
 12. The exhaust gas treatment system of claim 9, wherein the porous inorganic compound layer has a BET specific surface of 50 m²/g or more and holds the noble metal within 50 μm deep from a top surface thereof. 